Rare Earth SmCo Magnets


1524120191118960.jpg

Sintered SmCo magnets

A samarium–cobalt (SmCo) magnet, a type of rare earth magnet, is a strong permanent magnet made of an alloy of samarium and cobalt. They were developed in the early 1960s based on work done by Dr. Karl Strnat and Dr. Alden Rey at Wright-Patterson AFB and the University of Dayton, respectively.

SmCo is argueably the best permanent magnet material commercially available, with remanence similar to neodymium magnets, but with higher temperature ratings and with superior temperature stability. There are two types of SmCo magnets, SmCo 1:5 and SmCo 2:17.


Manufacturing Process

Both the types of SmCo magnets are manufacture by powder metallurgy. The raw materials are melted in a furnace and cast into thin sheet or ingot. The material is crushed and then pulverized by ball milling or by jet milling. The powder is then oriented with external magnetic field and pressed into blocks or near net shape. Final properties and density are achivied in following sintering and heat treatments. The blocks are then cut to shape and magnetized.


SmCo 1:5professional magnet supplier, magnet product manufacturer, NdFeB magnets, magnetic filter, SmCo magnets,Ceramic Magnets, AlNiCo Magnets,flexible rubber magnets, magnetic powder, magnetic strip, magnetic sheet, magnetic roll, daily use magnetsmagnetic sheet,AlNiCo magnets,magnetic filter

As the nomination indicates, the samarium–cobalt 1:5 magnet alloys (generally written as SmCo5, or SmCo 1:5) have one atom of rare earth samarium per five atoms of cobalt. By weight this magnet alloy will typically contain 36% samarium with the balance cobalt. Sometimes Prasedymium is alloyed to increase the remanence. The energy products of these samarium–cobalt alloys range from 16 MGOe to 25 MGOe, that is, approx. 128 - 200 kJ/m3. Contrary to SmCo 2:17 magnets, the 1:5 magnets are relatively easy to magnetize and saturation magnetization can be achieved with a moderate magnetizing field. Therefore, 1:5 magnets are easier to calibrate to a specific magnetic field than the SmCo 2:17 magnets.


SmCo 2:17professional magnet supplier, magnet product manufacturer, NdFeB magnets, magnetic filter, SmCo magnets,Ceramic Magnets, AlNiCo Magnets,flexible rubber magnets, magnetic powder, magnetic strip, magnetic sheet, magnetic roll, daily use magnetsmagnetic sheet,AlNiCo magnets,magnetic filter

These alloys (written as Sm2Co17, or SmCo Series 2:17) are age-hardened with a composition of two atoms of rare-earth samarium per 13–17 atoms of transition metals (TM). The TM content is rich in cobalt, but contains also other metals such as iron and copper. Other elements like Zirkonium and Hafnium etc. may be added in small quantities to achieve better heat treatment response. The maximum energy products of these alloys range from 20 to 32 MGOe, what is about 160-260 kJ/m3. These alloys have the best reversible temperature coefficient of remanence of all rare-earth alloys, typically being -0.03%/°C.

In Sm2Co17 magnets, the coercivity mechanism is based on domain wall pinning (in contrary to SmCo 1:5 and NdFeB where it’s nucleation). The purpose of alloying and heat treatment is to create a microstructure inside the magnets which impede the domain wall motion and thereby resist the magnetization reversal process.


Magnetic Properties of SmCo:

MaterialCodeRemanence BrCoercivity ForceIntrinsic CoercivityMaximum EnergyCurieMaximum Operating






ForceProduct BhmTemperatureTemperature


BrbHciHc(BH)maxTCTW


TKGsKA/mKOeKA/mKOeKJ/m 3MGOe° C° C
Sintered

YX-180.85-0.98.5-9.0620-6487.8-8.21194-151315-19127-14316-18750250
SmCo1: 5YX-200.92-0.969.2-9.6653-7178.2-9.01194-151315-19150-16719-21750250

YX-240.96-1.09.6-10.2730-7709.2-9.71194-151315-19175-19022-24750250













YXG-240.95-1.029.5-10.2637-7328.0-9.21433-199018-25175-19022-24800350
SmCo2: 17YXG-261.02-1.0510.2-10.5748-7969.4-10.01433-199018-25195-21524-26800350

YXG-281.05-0.0810.5-10.8756-7969.5-10.01433-183118-25205-22026-28800350

YXG-28B1.02-1.1010.2-11.04205.2-5.6440-5205.5-6.5205-22026-28800350

YXG-301.08-1.1010.8-11.07809.8-10.5955-119518-25220-24028-30800350

YXG-30B1.08-1.1510.8-11.54205.2-5.6440-5205.5-6.5220-24028-30800350
Bonded

Yb-60.44.02803.58001030-504-6-120
smCo1: 5Yb-100.55.03204.08001050-656-8-120

YbG-100.66.03604.58001065-808-10-120
smCo2: 17YbG-120.77.04005.08001085-9510-12-120

The typical physical properties of SmCo magnets:
Curie Temp.
Tc

° C

800-850

Coeff. Of thermal expansion

C //

1/° C

~8× 10 -5

Density

D

g/cm 3

8.3-8.5

C⊥

1/° C

~11× 10 -5

Recoil permeability

rec


1.00-1.05

Regidity Strength

N/m 2

~1.5× 10 8

Max. working Temp.

Tmax

° C

350

Compress Strength

N/m 2

~8× 10 8

Electrical Resistivity


Ω Cm

~8.6× 10 -5

Tensile Strength

N/m 2

~3.5× 10 7

Vickers Hardness

Hv


500-600

Young' s modulus

N/m 2

~1.2× 10 11

Thermal Conduct Rate


W/mK

~12

Magnetization field Ha

kA/m

≥ 1600